bainite

美 ['beɪnaɪt]英 ['beɪnaɪt]

n.【冶】贝菌体
网络贝氏体；变韧铁；贝茵体

bainite

bainite

英-汉网络释义

bainite

n.

1.【冶】贝菌体,贝氏体

1

Bainite also occurs during thermal treatments at cooling rates too fast for pearlite to form , yet not rapid enough to produce martensite .

贝氏体期间也发生在热处理冷却速度太快珍珠岩形式，还没有足够的迅速产生马氏体。

7

8

The microstructure of the weld bonds is a combination of martensite , lower bainite and retained austenite.

焊接熔合区组织为马氏体 +下贝氏体 +残余奥氏体；

9

Essentially , hardness lag of the alloyed Bainite ductile cast iron resulted from solute drag-like effect .

贝氏体球墨铸铁有性能滞后现象，其实质是溶质类拖曳作用。

10

MPa grade RPC steel is the recently developed new generation steel, which has ultra-fine bainite and better mechanical properties .

RPC 钢是一种具有超细的贝氏体组织和较好力学性能的新一代钢铁材料。

11

Solute atoms may be segregated in pre-bainite period and solute - depleted region may be nucleation site .

贝氏体预相变期发生溶质原子偏聚，贫溶质区即形核位置。

12

The formation of upper bainite ferrite was investigated with TEM, The much smaller lamellate subunits was observed .

观察到贝氏体条由更小的薄片状亚单元组成。

13

With the isothermal holding time prolonged , the thick rod-like upper bainite associated and gradually developed into featherlike bainite.

随着等温时间的进一步延长，粗棒状上贝氏体平行排列组合具有近似羽毛状；

15

Influence of different heat treatment process on microstructure and properties of bainite steel has been investigated .

研究热处理对新型贝氏体钢的组织与力学性能的影响。

17

By controlling knock-out time, bainite structure was obtained in the as - cast low - carbon ductile iron cast with EPC process.

采用消失模铸造工艺，经准铸态贝氏体工艺处理后，得到了贝氏体组织。

18

When the crack meets the hard phase bainite, it spreads along the edge of the bainite.

裂纹在扩展过程中遇到硬质相贝氏体时沿其边缘行走。

19

The intermedium temperature microstructure of medium carbon alloy steel is upper and lower bainite .

中碳合金钢的中温转变组织只有上、下贝氏体。

20

The strengthening of X100 pipeline steel mainly depend on bainite transformation and precipitation strengthening .

X100 管线钢的强化机制主要为组织细化和贝氏体相变强化。

21

The effect of austenitizing temperature on structure and properties of vanadium bainite ductile cast iron is studied in present research .

研究奥氏体化温度对含钒贝氏体球墨铸铁组织和性能的影响。

24

26

Ferrite (F ) zone, pearlite (P ) zone, bainite (B) zone and martensite(M) zone were found on both CCT diagrams.

两种 CCT 曲线上均有铁素体区（F ）、珠光体区（P ）、贝氏体区（B ）和马氏体区（M ）。

28

The nature of bainite changes as the transformation temperature is lowered .

性质的改变贝氏体转变温度降低。

29

Brief Discussion on Nucleation and Growth in Bainite Formation--Reply to Prof. Kang Mo-kuang et al.

简论贝氏体相变的形核与长大 --复康沫狂教授等。

30